Wood Imitation blended polyol
Home » Busniess » Polyurethane (PU) » Wood Imitation blended polyol
Wood Imitation blended polyol Wood Imitation blended polyol

loading

Wood Imitation blended polyol

Availability:

A.Furniture 

Item

Index

Index

Blowing Agent

HCFC-141b

HFC-245FA

Material Temperature

20~25℃

20~25℃

POL/ ISO Ratio

1:1 ~1.2pbw

1:1.1~1.2pbw

Mold Temperature

40~45℃

35~45℃

Cream Time

15~40s

15~25s

Gel Time

70~160s

70~100s

Tack Free Time

90~210s

100~130s

Free Rise Density

80~120 kg/m3

80~110 kg/m3

 *The actual reactivity characteristics may be adjusted according to process conditions and clients’requirements.

*Isocyanate is polymeric MDI

 

B.Line /Decoration

Item

Index

Index

Blowing Agent

HCFC-141b

HFC-245FA

Material Temperature

20~25℃

20~25℃

POL/ ISO Ratio

1:1 ~1.2pbw

1:1.1~1.2pbw

Mold Temperature

40~45℃

35~45℃

Cream Time

10~20s

10~20s

Gel Time

50~100s

50~100s

Tack Free Time

80~160s

80~160s

Free Rise Density

50~80 kg/m3

50~80 kg/m3

*The actual reactivity characteristics may be adjusted according to process conditions and clients’requirements.

*Isocyanate is polymeric MDI

 

C.PU trowel

Item

Index

Index

Blowing Agent

HCFC-141b

Water

Material Temperature

20~25℃

20~25℃

POL/ ISO Ratio

1:1pbw

1:1.5pbw

Mold Temperature

25℃

25℃

Cream Time

10-20s

10-20s

Gel Time

40-60s

40-60s

Tack Free Time

50-90s

50-90s

Free Rise Density

35-55 kg/m3

35-55 kg/m3

*The actual reactivity characteristics may be adjusted according to process conditions and clients’ requirements.

*Isocyanate is polymeric MDI